产品服务热线:0086-416-8301559   8302059
邮箱:563117193@qq.com
Copyright© 2017 锦州万得焊材有限公司 all rights reserved.   
辽ICP备17014853号-1  技术支持中企动力

Carbon Steel

Low Alloy Steel

High Strength Steel

Stainless Steel

Hard Surfacing

Submerged Arc Welding Wire

Electrode

Stainless Steel Strip

WD-SJ101埋弧焊用烧结焊剂WD-SJ101 SAW FLUX

符合标准:GB/T5293-1999 F4A4-H08A AWSA5.17-2004F6A4-EL8 F5A4-H10Mn2 F7A4-EH14GB/T12470-2003 F55A2-H08MnMoA AWSA5.23-2004 F8A0-EA2-A1 认证机构:ABS,CCS,DNV,GL,LR
没有此类产品
产品描述

符合标准:

GB/T 5293-1999 F4A4-H08A AWS A5.17-2004 F6A4-EL8 F5A4-H10Mn2 F7A4-EH14

GB/T 12470-2003 F55A2-H08MnMoA AWS A5.23-2004 F8A0-EA2-A1

 

认证机构:ABS, CCS, DNV, GL, LR

 

说明:WD-SJ101是氟碱型碱性烧结焊剂,碱度约1.8(BIIW),为球形颗粒,粒度为10-60目。焊剂的熔敷金属纯净,具有较高的低温冲击韧性,焊缝成形美观,脱渣容易。可用于单丝、双丝、多丝和窄间隙埋弧自动焊。可交直流两用,直流时焊丝接正极。

 

用途:可用于船舶、压力容器、贮罐、钢结构、桥梁、螺旋焊管等结构的对接及角接焊缝。

 

焊剂参考成分(%):

 

 

熔敷金属力学性能:

 

 

注意事项:

1、焊剂如果受潮,在使用前须经300~350℃烘焙2小时。

2、焊接处须清除铁锈、油污、水分等杂质。

 

WD-SJ101 Agglomerated Flux For S.A. Welding
 
Standards:EN760 A FB 1 67 AC H5
 
GB/T 5293-1999   F4A4-H08A AWS A5.17-2004   F6A4-EL8
F5A4-H10Mn2 F7A4-EH14
 
GB/T 12470-2003   F55A2-H08MnMoA AWS A5.23-2004   F8A0-EA2-A1
 
Approvals: ABS, CCS, DNV, GL, LR
 
 
Introduction
 
WD-SJ101 is an agglomerated fluoride-basic type flux with a basicity index of BIIW 1.8. The flux is spherical granular, grain size is from 10 to 60 mesh. As weld metal is very purity, the diffusible hydrogen content in deposited metal is less than 5ml/100g, so has very good toughness at the low temperature, therefore, crack resistance is extremely high. WD-SJ101 assures excellent weldability, bead appearance is beautiful, slag is extremely easy to remove. WD-SJ101 is suitable for submerged-arc twin-wire, tandem and multi-wire welding as well as for welding with the two-run technique. The special production method ensures that the flux  has low moisture pick-up and granular stability. Flux shall be capable of meeting the applied requirements. As the bulk density is low, so is the consumption rate. 
 
Applications
 
Flat butt and fillet welding of mild and high tensile strength steels for frames, bridges, pipes, pressure vessels, rolling stock, offshore structures and ships.
 
Characteristics
 
It has excellent welding technology properties for fillet welding of thick plates. Regularly shaped welds are deposited without reduction of area or interface notches. Blowholes scarcely
occur. Satisfactory weldability and mechanical properties are obtained with heat input.
 
Main Constituents (%)
 
 
Typical mechanical property of deposited metal
 
 
Typical chemical composition of deposited metal (%)
 
 
Notice:
 
1. Flux should be redried at 300~350°C for 2 hours.

 

2. All dust, oil and rust should be removed. 